Effect of Addition of Ce on Fe–K Mixed Oxide Catalyst in Dehydrogenation of Ethylbenzene
Ethylbenzene dehydrogenation Cerium addition Iron oxide catalyst Surface area
2010/9/8
Dehydrogenation of ethylbenzene was evaluated with Fe–K and Fe–Ce–K mixed oxide catalysts to examine the addition effect of Ce. Fe–Ce mixed oxide was prepared by co-precipitation of Fe and Ce nitrate ...
Steam Reforming of Ethanol over Co/La1-xSrxBO3 (B = Al, Cr, Mn, Fe) Catalysts
Steam reforming Ethanol Hydrogen production Perovskite Lattice oxygen
2009/8/4
The steam reforming of ethanol for producing hydrogen was evaluated over 5 wt% Co catalysts supported on perovskite-type oxides, La1-xSrxBO3 (B = Al, Cr, Mn, Fe, x = 0-0.2) at 823 K with a molar H2O/C...
乙烷部分氧化超细Fe-Mo-O催化剂的研究
溶胶-凝胶技术 乙烷部分氧化 超细Fe-Mo-O催化剂
2008/3/2
摘要采用溶胶-凝胶法制备了Fe-Mo-O催化剂,用XRD、TEM、BET、IR、TPR、TPD和微反等技术研究了催化剂晶体结构、表面构造、晶格氧活泼性、化学吸附和乙烷部分氧化反应性能。Fe-Mo-O复合氧化物催化剂是由超细微粒组成,微粒粒径约10 nm~20 nm,比表面积为48.1 m2/g。催化剂表面由Lewis碱位(Mo=O键的端氧和Fe-O-Mo键中的桥氧)及Lewis酸位构成。乙烷能以甲...
丙烯环氧化制环氧丙烷Fe-Al-P-O催化剂的研究
溶胶-凝胶法 Fe-Al-P-O催化剂 丙烯 环氧化 环氧丙烷
2008/3/2
摘要用溶胶-凝胶法制得了Fe-Al-P-O催化剂,采用IR、XRD、TEM、BET、TPR和微反等技术研究了催化剂的物化性质和反应性能。实验结果表明,Fe1/2-Al1/2-PO4由10 nm左右 FePO4和AlPO4微晶组合而成,其晶格氧的活泼性大于单纯FePO4,AlPO4在Fe1/2-Al1/2-PO4中起到分散FePO4微晶的作用;Fe1/2-Al1/2-PO4的反应性能与原料气组成密切...
Fe/炭黑、Ni/炭黑催化剂对渣油加氢反应的影响
催化剂载体 炭黑 渣油 生焦
2008/3/2
摘要使用模型化合物在微型反应釜中研究了载体炭黑对渣油内部氢转移反应的影响。结果表明,炭黑可以明显地促进四氢萘到蒽的氢转移反应。使用等体积浸渍法制备了Fe/炭黑、Ni/炭黑催化剂并对Fe/炭黑催化剂进行了XRD、SEM表征,结果表明,金属硫化物附着在炭黑颗粒的表面,直径为1μm左右。在高压反应釜中研究了载体炭黑和以炭黑为载体的催化剂对克拉玛依常压渣油430℃加氢反应的影响,并于传统的水溶性分散型催化...