搜索结果: 76-90 共查到“知识库 材料合成与加工工艺”相关记录935条 . 查询时间(5.327 秒)
Morphological features of retained austenite in thermo-mechanically processed C-Mn-Si-Al-Nb-Ti multiphase steel
Morphological austenite C-Mn-Si-Al-Nb-Ti multiphase steel
2010/8/12
Development of multiphase steels is one of the biggest achievements of contemporary metallurgy in the field of advanced materials for motorization. They are C-Mn-Si, C-Mn-Si-Al, C-Mn-Al-type low-alloy...
塑料注射成形充填模拟中,采用GLS(Galerkin/least-squares)法能实现速度、压力同次插值时稳定地求解速度场、压力场,在能量场方程的求解中采用GGLS(Galerkin gradient least-squares)/SUPG(streamline upwind/Petrov-Galerkin)法能得到稳定的温度场数值解,其中SUPG法抑制对流占优导致的数值震荡问题,GGLS法消...
A method for setting variables in Super Plastic Forming process
method setting variables Super Plastic Forming process
2010/8/12
Superplastic forming or SPF is a technique of presswork high temperature of metal sheets that falls in hot blow forming processes. The elongation obtained with this technology exceeds 100% and limits ...
Springback prediction in V-die bending: modelling and experimentation
Springback prediction V-die bending modelling experimentation
2010/8/12
Spring-back is a common phenomenon that occurs in sheet metal bending after unloading due to elastic recovery. It could be defined in terms of spring-back ratio K (the ratio between the produced and d...
为了解决传统复合钎料制备中强化颗粒容易粗化的问题,提高无铅复合钎料的性能,选用共晶Sn-3.5Ag、Sn-3.0Ag-0.5Cu钎料作为基体,3种不同类型具有纳米结构的有机-无机笼型硅氧烷齐聚物(POSS) 颗粒作为增强相而制成复合钎料。研究了复合钎料的铺展性能、钎焊接头的力学性能和抗蠕变性能。结果表明,复合钎料的润湿性能均优于基体钎料的润湿性能,复合钎料钎焊接头的剪切强度和蠕变断裂寿命均明显提高...
碳纤维增强金字塔点阵夹芯结构的抗压缩性能
复合材料 点阵夹芯 金字塔 压缩性能
2010/9/15
提出了一种碳纤维增强复合材料点阵夹芯结构的一体化成型工艺方法。该方法克服了传统夹芯结构面板与芯子之间因需要二次粘接或焊接的方法所带来弱界面的缺点。将纤维杆两端埋入面板内,使面板与芯子成为一体而不存在明显的界面。对用该方法制备的碳纤维增强金字塔点阵夹芯板进行平压试验,研究发现随着载荷的增加,纤维杆发生弹性屈曲并在中间部位出现断裂。理论分析了点阵夹芯结构平压载荷下的弹性模量和纤维杆极限屈曲载荷。通过与...
超重力下燃烧合成TiB2-TiC共晶复合陶瓷
TiB2-TiC复合陶瓷 燃烧合成 超重力 快速凝固 共晶转变
2010/9/15
采用超重力下燃烧合成技术,制备出TiB2-TiC共晶复合陶瓷。XRD、SEM与EDS结果表明,复合陶瓷主要由大量细小的TiB 2片晶均匀分布于TiC基体上的共晶组织构成,而富钛ε碳化物(Ti , Cr)C1-x则断续分布于TiC基体间,同时在基体中还孤立分布着少量的、形态不规则的α-Al2O3晶粒或Al2O3-ZrO2共晶团组织。高温化学反应使所有产物均呈液态,且超重力的引入诱发熔体内部Stock...
离子交换法制备ZrO2∶Eu 3+纳米晶及其发光特性
ZrO2∶Eu 3+纳米晶 离子交换法 发光性质
2010/3/2
以强碱性阴离子交换树脂为沉淀剂, 采用离子交换法制备了ZrO2∶Eu 3+纳米晶. 通过XRD, TEM,HRTEM和EDS等对晶体的结构、形貌及化学成分进行了表征, 利用3D荧光光谱、激发光谱和发射光谱研究了Eu3+在ZrO2纳米晶中的发光性质. 结果表明, 焙烧温度在800℃以下所得的ZrO2∶Eu 3+纳米晶主要为四方结构, 晶粒尺寸约为5-20 nm, 随着焙烧温度的升高, 样品的晶结构发...
Fabrication and characteristics of porous germanium films
germanium porous structured film visible photoluminescence
2010/1/19
Porous germanium films with good adhesion to the substrate were produced by annealing GeO2 ceramic films in H2 atmosphere. The reduction of GeO2 started at the top of a film and resulted in a Ge layer...
利用热压缩实验, 研究了中碳钢回火马氏体在700 ℃/0.01 s-1条件下变形时的组织演变规律, 分析了渗碳体粒子状态的影响. 实验结果表明: 中碳钢回火马氏体热变形过程中, 发生了渗碳体粒子粗化和铁素体动态再结晶, 形成由微米级的等轴铁素体晶粒与均匀分布的渗碳体粒子组成的超细化(α+θ)复相组织. 与静态回火相比, 形变促进Fe原子和C原子的扩散, 使渗碳体粒子粗化动力学提高2-3个数量级. ...
316L不锈钢热加工硬化行为及机制
316L不锈钢 热加工硬化 Crussard-Jaoul分析法 动态再结晶 孪晶
2010/3/4
在Gleeble-1500热模拟试验机上, 通过高温压缩实验对316L不锈钢的热加工硬化特点和机制进行了研究. 根据Ludwik幂函数模型对实验数据进行了非线性拟合, 并用 Crussard-Jaoul分析法计算了Ludwik幂函数模型的n值. 实验结果表明: 316L不锈钢在热变形过程中易发生加工硬化, 真应力-应变曲线上未出现应力峰值; 热变形过程中发生了部分动态再结晶, 这一不完全的软化机制...
TC1和TC4钛合金腐蚀加工溶解行为研究
TC1钛合金 TC4钛合金 腐蚀加工 电化学行为
2013/9/30
测试了TC1和TC4钛合金在氢氟酸-硝酸溶液中腐蚀加工的E-t曲线和极化曲线,分析了腐蚀加工过程的速率变化,观察了腐蚀加工形貌。在氢氟酸-硝酸腐蚀加工液中,极化曲线呈现活化-钝化特征,氢氟酸浓度较高时,硝酸浓度增大到一定值后,极化曲线呈现自钝化倾向。钝化膜的生成速率和厚度由氢氟酸和硝酸体积比决定,氢氟酸和硝酸体积比为1∶2时,腐蚀加工速率最大。腐蚀加工初期钛合金表面氧化膜被破坏,自腐蚀电位迅速变负...
采用辐射的方法对天然淀粉进行接枝改性,将一定量的绝干玉米淀粉与DMC的水溶液均匀混合,在60Co-γ辐射场中辐射后,经烘干、粉碎、离心萃取制备阳离子接枝淀粉。研究反应介质、预聚物配比、辐射剂量及辐射剂量率对样品制备的影响,并分析了产生这些影响的原因,得出制备此种阳离子接枝淀粉的最佳工艺参数:反应介质(水)配比0.28、预聚物配比0.06、辐射剂量6kGy、辐射剂量率10Gy/min。
Application of powder injection moulding and extrusion process to manufacturing of Ni-YSZ anodes
Composites Powder metallurgy Sintering
2009/12/14
Purpose: Investigation of the Ni-YSZ cermets for anode supported solid oxide fuel cells (SOFC) prepared by extrusion or powder injection moulding process, sintered and reduced of NiO-YSZ.
Design/meth...
Fabrication of nano-structured materials by high-pressure sintering
Powder metallurgy Metal sintering Nanomaterials Crystallite size
2009/12/2
Purpose: The aim of this work was to fabricate nanocrystalline powders and high-density bulk materials using a sintering
method with limited grain growth so as to maintain nanocrystalline structure o...